RUBBER EXTRUSION

CODE USE SPECIFICATION CERTIFICATION density
gr/cm³		 hardness
IRHD		 breaking
load
MPa		 extens.
%		 tearing
N/cm		 compression
E101 Extrusion in atoxic black rubber
suitable for the passage of drinking water.
Operative temperature -20 +100 °C		 Circolare N° 102 D.M.
del 02/12/78
UNI 9028		 CE.RI.SIE 1.18±0.05 75±5 min.
11.5		 min.
250		 min.
300		 max. 20
E107 Extrusion in atoxic black rubber
suitable for the passage of drinking water.
Operative temperature -20 +100 °C		 KTW
CSTB
KIWA		 DVGW
CSTB
KIWA		 1.23±0.05 75±5 min.
9		 min.
200		 min.
200		 max. 20
E109 Extrusion in black rubber
suitable for the passage of water.
Temp. esercizio -20 +150 °C		 - - 1.17±0.05 75±5 min.
9		 min.
200		 min.
200		 max. 40
E113 Extrusion in atoxic black rubber
suitable for the passage of drinking water.
Temp. esercizio -20 +100 °C		 KTW
W270
WRC		 DVGW
Hygiene Institut
WQC		 1.35±0.05 75±5 min.
9		 min.
200		 min.
200		 max. 20
WP Extrusion in black rubber
suitable for the passage of water. Temp. esercizio -20 +70 °C		 KTW
WRC		 DVGW
WQC		 1.00±0.05 75±5 min.
9		 min.
100		 min.
200		 max. 50
E171 Extrusion in atoxic black rubber
suitable for the passage of drinking water.
Operative temperature -20 +100 °C		 - - 1.17±0.05 75±5 min.
9		 min.
250		 min.
300		 max. 50
E175 Extrusion in atoxic black rubber
suitable for the passage of drinking water.
Operative temperature -20 +100 °C		 - - 1.22±0.05 75±5 min.
9		 min.
250		 min.
300		 max. 60
E176 Extrusion in atoxic black rubber
suitable for the passage of drinking water.
Operative temperature -20 +100 °C		 - - 1.31±0.05 75±5 min.
7		 min.
200		 min.
200		 max. 75
E177 Extrusion in atoxic black rubber
for gaskets.		 - - 1.31±0.05 85±5 min.
7		 min.
250		 min.
250		 max. 50
HG 102 Extrusion in atoxic black rubber
suitable for the passage of drinking water according to German rules.
Operative temperature -20 +100 °C		 KTW
KIWA		 DWGW
KIWA
 1.22±0.05 75±5 min.
9		 min.
250		 min.
250		 max. 20
E 140 Extrusion in dielectric black rubber.
Puncture voltage KV 6.
Dielectric strenght KV/mm 2.3		 CEI 15-1 CE.RI.SIE 1.38±0.05 75±5 min.
5		 min.
300		 min.
200		 max. 20
N 202 Extrusion in nitrile black rubber.
Suitable for the passage of fuels for trucks.
Operative temperature -10 +70 °C		 - - 1.25±0.05 75±5 min.
10		 min.
250		 min.
250		 max. 50
N 216 Extrusion in nitrile black rubber.
Suitable for the passage of oils, emulsified
water, gas for cars.
Operative temperature -10 +70 °C		 - - 1.27±0.05 80±5 min.
10		 min.
150		 min.
300		 max. 5
N 217 Extrusion in nitrile black rubber.
Suitable for the passage of fuel oils for burners.		 ISO 6806 - 1.41±0.05 75±5 min.
9		 min.
250		 min.
300		 max. 50
N 220 Extrusion in antiozonant nitrile black rubber. Suitable for the passage of oils, emulsified water.
Operative temperature -40 +125 °C		 - - 1.35±0.05 75±5 min.
9		 min.
250		 min.
300		 max. 60
N 230 Extrusion in nitrile black rubber.
Suitable for the passage of kerosene.
Operative temperature  -10 +70 °C		 - - 1.40±0.05 70±5 min.
9		 min.
200		 min.
300		 max. 50
S 320 Extrusion in antiabrasive styrene black rubber. - - 1.24±0.05 75±5 min.
10		 min.
250		 min.
300		 max. 65